Nickel Alloy Plate
Available thicknesses for Alloy 625:
|1 1/4"||1 1/2"||1 3/4"||2"||2 1/2"||3"|
An Austenitic Nickel-Chromium-Molybdenum-Niobium Alloy with Outstanding Corrosion Resistance and High Strength from Cryogenic Temperatures to 1800¡ã¹ó (982¡ã°ä)
Specification Sheet Overview
for Alloy 625 (UNS N06625)
W. Nr. 2.48161:
Alloy 625 is an austenitic nickel-chromium-molybdenum-niobium alloy possessing a rare combination of outstanding corrosion resistance coupled with high strength from cryogenic temperatures to 1800¡ã¹ó (982¡ã°ä).
The strength of Alloy 625 is derived from the solid-solution hardening of the nickel-chromium matrix by the presence of molybdenum and niobium. Therefore, precipitation-hardening treatments are not required.
The chemical composition of Alloy 625 is also responsible for its outstanding corrosion resistance in a variety of severe operating environments along with resistance to oxidation and carburization in high temperature service. The alloy is resistant to pitting, crevice corrosion, impingement corrosion, intergranular attack and is almost immune to chloride stress corrosion cracking.
Alloy 625 can be easily welded and processed by standard shop fabrication practices.
- Aerospace Components ¨C bellows and expansion joints, ducting systems, engine thrust-reversers, turbine shroud rings
- Air Pollution Control ¨C chimney liners, dampers, flue gas desulfurization (FGD) components
- Chemical Processing ¨C equipment handling both oxidizing and reducing acids, super-phosphoric acid production
- Marine Service ¨C steam line bellows, Navy ship exhaust systems, submarine auxiliary propulsion systems
- Nuclear Industry ¨C reactor core and control rod components, waste reprocessing equipment
- Offshore Oil and Gas Production ¨C waste flare gas stacks, piping systems, riser sheathing, sour gas piping and tubing
- Petroleum Refining ¨C waste flare gas stacks
- Waste Treatment ¨C waste incineration components
Weight % (all values are maximum unless a range is otherwise indicated)
|Chromium||20.0 min.-23.0 max.||Phosphorus||0.015|
|Molybdenum||8.0 min.-10.0 max.||Sulfur||0.015|
|Niobium (plus Tantalum)||3.15 min.-4.15 max.||Titanium||0.40|
|Carbon||0.10||Cobalt (if determined)||1.0|
Specific Heat0.102 BTU/lb-¡ã¹ó (32-212¡ã¹ó)
427 J/kg-¡ãK (0-100¡ã°ä)
Modulus of Elasticity30.1 x 106 psi
Thermal Conductivity 200¡ã¹ó (100¡ã°ä)75 BTU/hr/ft2/´Ú³Ù/¡ã¹ó
Melting Range2350 ¨C 2460¡ã¹ó
1290 ¨C 1350¡ã°ä
Electrical Resistivity50.8 Microhm-in at 70¡ã°ä
128.9 Microhm-cm at 210¡ã°ä
|Mean Coefficient of Thermal Expansion
|200||93||7.1 x 10-6||12.8 x 10-6|
|400||204||7.3 x 10-6||13.1 x 10-6|
|600||316||7.4 x 10-6||13.3 x 10-6|
|800||427||7.6 x 10-6||13.7 x 10-6|
|1000||538||7.8 x 10-6||14.0 x 10-6|
|1200||649||8.2 x 10-6||14.8 x 10-6|
|1400||760||8.5 x 10-6||15.3 x 10-6|
|1600||871||8.8 x 10-6||15.8 x 10-6|
|1700||927||9.0 x 10-6||16.2 x 10-6|
Typicals Values at 68¡ã¹ó (20¡ã°ä)
in 2 in.
|psi (min.)||(MPa)||psi (min.)||(MPa)||% (min.)||(max.)|
The highly alloyed chemical composition of Alloy 625 imparts outstanding corrosion resistance in a variety of severely corrosive environments. The alloy is virtually immune to attack in mild conditions such as the atmosphere, fresh and sea water, neutral salts and alkaline solutions. Nickel and chromium provide resistance to oxidizing solutions and the combination of nickel and molybdenum supply resistance in non-oxidizing environments. Molybdenum also makes Alloy 625 resistant to pitting and crevice corrosion, while niobium acts as a stabilizer during welding to prevent intergranular cracking. The high nickel content of Alloy 625 makes it virtually immune to chloride stress corrosion cracking.
The alloy resists attack by mineral acids such as hydrochloric, nitric, phosphoric and sulfuric, and to alkalis and organic acids in both oxidizing and reducing conditions.
Corrosion-resistance of nickel alloys in 24-hour tests in boiling 40% formic acid.
Corrosion-resistance of nickel alloys in four 24-hour tests in boiling acetic acid
Resistance of nickel alloys to impingement attack by seawater at 150 ft/sec (45.7 m/s)
The comparative PREN number for alloy 625 is shown in the table below.
Pitting resistance equivalency numbers (PREN) for corrosion resistant alloys
|316 Stainless Steel||12||17||2.2||—||—||—||20.4|
|317 Stainless Steel||13||18||3.8||—||—||—||23.7|
The oxidation and scaling resistance of Alloy 625 is superior to a number of heat resistant austenitic stainless steels such as 304, 309, 310 and 347 up to 1800¡ã¹ó (982¡ã°ä) and under cyclic heating and cooling conditions. Above 1800¡ã¹ó (982¡ã°ä), scaling can become a restrictive factor in service.
Alloy 625 can be easily welded and processed by standard shop fabrication practices, however because the high strength of the alloy, it resists deformation at hot-working temperatures.
The hot-working temperature range for Alloy 625 is 1650 ¨C 2150°F (900 ¨C 1177°C). Heavy working needs to occur as close to 2150°F (1177°C) as possible, while lighter working can take place down to 1700°F (927°C). Hot-working should occur in uniform reductions to prevent duplex grain structure
Alloy 625 can be cold-formed by the standard shop fabrication practices. The alloy should be in the annealed condition. Work hardening rates are higher than the austenitic stainless steels.
Alloy 625 can be readily welded by most standard processes including GTAW (TIG), PLASMA, GMAW (MIG/MAG), SAW and SMAW (MMA). A post weld heat treatment is not necessary. Brushing with a stainless steel wire brush after welding will remove the heat tint and produce a surface area that does not require additional pickling.
Alloy 625 should preferably be machined in the annealed condition. Since Alloy 625 is prone to work¨Chardening, only low cutting speeds should be used and the cutting tool should be engaged at all times. Adequate cut depth is necessary to assure avoiding contact with the previously formed work-hardened zone.
NOTE: The information and data in this product data sheet are accurate to the best of our knowledge and belief, but are intended for informational purposes only, and may be revised at any time without notice. Applications suggested for the materials are described only to help readers make their own evaluations and decisions, and are neither guarantees nor to be construed as express or implied warranties of suitability for these or other applications.